Description:
Liqui Moly Underseal Black
This Liqui Moly Underseal Black is a fast-drying, rubber and resin-based protective layer that provides excellent abrasion-resistant corrosion protection and sound absorption. It forms a permanently elastic film that guards against stone chipping and can be easily painted over with commercially available paint systems.
Ideal for coating bare and painted surfaces, particularly on vehicle underbodies, it is perfect for repairing or supplementing existing PVC or rubber/resin-based coatings. Especially suited for treating hard-to-reach areas like angles, corners, and edges, where rust tends to form.
Benefits:
- Very good adhesion on various substrates
- Very good resistance to weathering, salt spray and abraded material
- Good stoneguard properties
Technical Information:
| Property | Specification |
|---|---|
| Base | Caoutchouc, Resins, Solvent, Filler |
| Form | Liquid |
| Curing / Setting | Evaporation of Solvents |
| Density at 20 °C | 1.02 kg/l (DIN 51757) |
| Cleaning | Solvent (Fresh), Mechanic (Dry) |
| Thinner | Solvent |
| Solids Content, 3 h at 120 °C | Ca. 50% (DIN 53216) |
| Viscosity at 20 °C | Ca. 48 Pas |
| Thermal Stability After Curing | -30 to +80 °C |
| Resistant After Curing (20 °C) | Water, Salt Spray, Oil, Light Acids and Base |
| Consumption | ±0.7 l/m² (At Approx. 700 µm Wet) |
| Skin Formation Time at 20 °C / 65% Relative Humidity | Ca. 45 min (±700 µm Wet) |
| Through-Drying at 20 °C / 65% Relative Humidity | Ca. 2 h (±700 µm Wet) |
| Re-Coatability | After Through-Drying |
| Salt-Spray Test | Up to 480 h (±700 µm) (DIN 50021) |
| Recommended Storage Temperature | +10 – +30 °C |
| Shelf Life in Original Sealed Container | 24 Months |
| Areas of Application | Various |